Round Bar ALCAST Aluminum Alloy in Strength and Corrosion Resistance

ALCAST aluminum alloy is an aluminum alloy that can be strengthened by heat treatment. The following are the characteristics of ALCAST aluminum alloy:

The chemical composition of ALCAST aluminum alloy:

Aluminum Al: balance

Silicon Si: ≤0.10

Iron Fe: ≤0.12

Copper Cu: 1.2~1.9

Manganese Mn: ≤0.06

Magnesium Mg: 1.9~2.6

Chromium Cr: 0.18~0.25

Zinc Zn: 5.2~6.2

Titanium Ti: ≤0.06

Other elements not specified: each: ≤0.05; Total: ≤0.15

ALCAST mechanical properties:

Tensile strength σb (MPa): ≤305

Elongation δ10 (%): ≥5

Density: 2.730g/cm.

Poisson's ratio: 0.33 at 20°C (68F)

.

Elastic modulus: tensile: 69.3GPa (10.1?106psi),

shear 26GPa (3.75?106psi),

compression 70.7GPa (10.3 ?106psi)

Note: Sample size of pipe mechanical properties at room temperature: Wall thickness/mm (all) Status: Aluminum and aluminum alloy drawn (rolled) seamless pipe (H32)

Specimen size: All

Formability and plasticity: ALCAST aluminum alloy has good formability and plasticity, making it easy to process into parts of various shapes and sizes. This makes it widely used in the manufacturing field.

Machinability: Due to its good plasticity and formability, ALCAST aluminum alloy also has good machinability during machining. This means that it can be machined through common machining methods such as milling, turning, drilling, etc.

Good operability: After annealing, ALCAST aluminum alloy can maintain good operability. This means that materials are easy to handle and handle during processing and assembly, improving production efficiency.